Ferrite Potential I-VSpectroscopy Polystyrene 3-hexylthiophene Gallium Molybdenum_disulfide ThinFilm Barium_titanate MLCC EFM Bmp Titanate DLaTGS StyreneBeads non_contact Solution light_emitting Temasek_Lab Dr.JurekSadowski Heat Growth ferromagnetic Magnets align Ito SPMLabs Alloy Phosphide temp_control HexagonalBoronNitride CHRYSALIS_INC Oxidation MembraneFilter INSPParis
Report image
If you found this image unacceptable, please let us know. We will review your report and take action if we determine this image is really unacceptable.
Collagen film phase change by temp
Scanning Conditions
- System: NX10
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan