DIWafer NiFe Writing NeodymiumMagnets Aggregated_molecules HexacontaneFilm Kevlar NUS VinylAlcohol Chloroform Switching blended polymers BaTiO3 ImideMonomer MultiferroicMaterials SrTiO3 MolybdenumDisulfide SSRM FastScan Photovoltaics fluorocarbon LightEmission ElectrostaticForceMicroscopy Pyroelectric Insulator Steps MultiLayerCeramicCapacitor MeltingPoint lithography HighAcpectRatio CrystalGrowing LiquidCrystal Tin disulfide LFM PFM
Report image
If you found this image unacceptable, please let us know. We will review your report and take action if we determine this image is really unacceptable.
Cast Iron surface change after Corrosion
Scanning Conditions
- System: NX10
- Scan Mode: Contact
- Cantilever: NSC36C (k=0.6N/m, f=65kHz)
- Scan Size: 50μm×50μm
- Scan Rate: 1.5Hz
- Pixel: 512×1024
- EC bias voltage: -0.266V